防止平板铸铁件侵入性气孔缺陷与浇注工艺参数关系的探讨
Investigation on Relationship Between the Intrusive Blowhole and the Gating Parameters of Plate Shaped Iron Castings
浏览(6392) 下载(0)
- DOI:
- 作者:
- 陈文平
- 作者单位:
- 北京机床研究所
- 关键词:
- 平板铸铁件;侵入性气孔;压力上升速度;液面上升速度;浇注参数
Plate iron castings; Intrusive blowhole; Rise rate of pressure; Rate of liquid iron ascending; Gating parameters
- 摘要:
- 当金型界面气体压力上升速度超过液态金属上升产生压力的速度,就会形成侵入性气孔缺陷。本文研究平板铸件铁液液面上升速度与金型界面气体压力等参数,及其与型砂的发气能力、透气能力存在的定量关系,确定透气性各要素之间也有着一定的数学关系。据此得出平板铸铁件浇注工艺参数的计算公式及图表,可作为防止侵入性气孔缺陷的工艺设计参考。
Blowhole defects are formed when the increment of gas pressure at the mold/metal interface exceeds that pressure generated by the liquid metal ascending. The quantitative relationship between the gas pressure in between mold/metal interface and the rate of the liquid metal ascendingand and the permeability of the mold were discussed. It was found that the mathematics quantitative relationships were existing in between the permeability parameters. And the calculation formula and tables of various parameters in gating system could be obtained, which could be used as the reference for preventing the blowhole defects.